RICERCA, ESPERIENZA, SVILUPPO E SERVIZIO: LE SOLIDE FONDAMENTA DELLA PROIND

Transcript

1 RICERCA, ESPERIENZA, SVILUPPO E SERVIZIO: LE SOLIDE FONDAMENTA DELLA PROIND RESEARCH, EXPERIENCE, DEVELOPMENT AND SERVICE: THE SOLID FOUNDATIONS OF PROIND Proind founded by its actual president Mr. Armando Settili, since in the seventies dealing in chemical products for the building industry and from its start the products were appreciated from the building industry, precasting and throught the resellers of special products in construction market. The production is a wide range of, mortars, additives, protective and waterproofing products to restore buildings as monuments, historical and industrial, to improve the quality and the durability of the concrete structures. To protect and restore there are five specific lines of products: ANDROMEDA SIRIO PEGASO GEMINI ORIONE Thanking its long experience Proind today it s a safe reference point for the buildings operators that found always complete and innovative answers for all their specific needings. The continuos research, constantly improved, has consented to reach important goals and commercial agreements throught its expansion in European Community and in differents countries, United States and Japan that are notoriously in the van of technology in prevention of the corrosion and in waterproofing of concrete structures. The high standard and the quality of Proind products (ISO 9002 certification), the particular attention and the care to the environment safety, the commercial seriousness and the high level service of the thecnical staff, are for sure elements that, with pride, Proind company is offering to all of his Customers. Proind wish that the products will help you to find the best solution to every matter in using additives to restore, release, waterproof and protect the concrete in the faster and cheapest way but also having the long lasting durability. We remain at your disposal in order to evaluate the best possible proposal. La PROIND fondata nel 1978 dall'attuale amministratore Armando Settili, opera nel settore edile della prefabbricazione, delle rivendite di materiali e prodotti speciali per l'edilizia, nonché nel settore del restauro delle opere civili, industriali e monumentali. La produzione della società comprende un'ampia gamma di additivi, disarmanti, protettivi ed impermeabilizzanti, per migliorare la qualità e la durabilità delle opere in calcestruzzo nonché per la protezione ed il restauro dei manufatti in cls con linee di prodotti specifiche quali: LINEA ANDROMEDA LINEA SIRIO LINEA PEGASO LINEA GEMINI LINEA ORIONE Grazie all'esperienza maturata, la PROIND è diventata un sicuro punto di riferimento per gli operatori edili che trovano in essa risposte esaustive ed innovative, per tutte le specifiche necessità. La continua ricerca in campo nazionale ed internazionale, ha permesso alla società di raggiungere importanti traguardi ed accordi commerciali anche attraverso l'espansione nei paesi della Comunità Europea ed in differenti paesi nel mondo, quali Stati Uniti e Giappone notoriamente all'avanguardia tecnologica nei settori prevenzione della corrosione ed impermeabilizzazione delle opere in calcestruzzo. La qualità dei prodotti (CERTIFICAZIONE ISO 9002) la particolare attenzione alla sicurezza ed all'ambiente, la serietà commerciale ed il servizio dello staff tecnico, sono sicuramente elementi che con orgoglio la PROIND propone a tutti i suoi Clienti. PROIND si augura che i prodotti offerti possano aiutare a trovare la migliore soluzione ai vostri problemi di additivazione, restauro, impermeabilizzazione, disarmo e conservazione del calcestruzzo, nel modo più rapido ed al contempo più economico e durevole possibile. Restiamo a disposizione per valutare insieme la migliore proposta. 2

2 ENTRA NELL UNIVERSO PROIND E ORIONE GEMINI

3 ANDROMEDA SIRIO PEGASO SCEGLI LA TUA COSTELLAZIONE.

4 LE NOSTRE LINEE OUR LINES ANDROMEDA Prodotti ad alta resistenza chimica HCR - High chemical resistance products SIRIO Malte cementizie antiritiro e a base calce - Formulati speciali - Fibre Controlled shrinkage, cement and lime based, mortars - Special compounds - Fibers PEGASO Prodotti impermeabilizzanti ad alto contenuto tecnologico Technological waterproofing products GEMINI Additivi per calcestruzzi e malte - Disarmanti Concrete and mortars additives - Release agents ORIONE Attrezzature varie Various fittings La migliore soluzione ai vostri problemi di additivazione, restauro, deumidificazione, impermeabilizzazione, disarmo, consolidamento e conservazione del calcestruzzo. The best solution to every matter in using additives, to restore, release, waterproof and protect concrete.

5 PROIND 6

6 INDICE PER LINEE LINES INDEX ANDROMEDA pag. 10_17 HCR Prodotti ad elevata resistenza chimica HCR - High chemical resistance products MCI MCI MCI 2020 VO 12 MCI MCI TM VCI SIRIOCEM PF SIRIOEPOS SIRIOEPOS SIRIOBETON HCR SIRIOBETON HCR MICROPOZ SIRIOBETON BME 17 SIRIO pag. 18_37 Malte cementizie antiritiro e a base calce Controlled shrinkage, cement and lime based, mortars SIRIOBETON RV - RV FINE SIRIOBETON FA SIRIOBETON RA SIRIOBETON FIX - R SIRIOBETON AC SIRIOBETON INZ SIRIOBETON BME SIRIOBETON PR SIRIOBETON PR MONO SIRIOBETON STOP SIRIOBETON FLEX M (SIRIORETE) INTOCAL INTOCAL RINZAFFO 27 SIRIOBETON IDR SIRIOBETON IDR RINZAFFO 28 RASOCAL (SIRIORETE) INTONACHINO ANTICO KALINZ Formulati speciali Special compounds SIRIOBETON ADD SIRIOBETON ADD SIRIOBETON ADD SIRIOBETON RAPID DUROKAL SFERUG PASTA DORIT 35 SIRIONET 35 SIRIOPEL 36 SOLVOIL 36 Fibre Fibers SIRIOFIBRE FIBRE IN POLIPROPILENE-SIRIOFIBRE/G 37 SIRIOFIBRE MICRO SIRIOFIBRE MICRO 10/A 20/A 37 FIBRE IN POLIACRILONITRILE 37

7 PEGASO pag. 38_53 Prodotti impermeabilizzanti ad alto contenuto tecnologico Technological waterproofing products Sottoquota Underground structures BENTOPAN BENTOGEO - BENTOGEO P BENTOPOL/PF 39 BENTOTITE WATER BAR BENTOTITE BIG KUNISEAL BENTOTITE PASTE HR LEAKMASTER SIRIOBETON STOP GIUNTOFLEX POLYPRIMER PER GIUNTOFLEX 45 SIRIOBETON BME GIUNTOROLL 46 SIRIOSEAL Sopraquota Above grade structures SIRIOSAN HYDROSTOP SIRIOBARRIERA SIRIOBARRIERA W SIRIOBARRIERA WR RESIVIL SIRIOCRYL - SIRIOCRYL E HYDROMAS SIRIOBIT 53 SOLVOIL 53 Accessori Accessories RETE PER KUNISEAL 42 CHIODI DI FISSAGGIO 40 e 42 (BENTOPAN - BENTOGEO-P - RETE PER KUNISEAL) RONDELLE DI FISSAGGIO 40 (BENTOPAN - BENTOGEO-P ) PISTOLA PER GIUNTOFLEX 46 GEMINI pag. 54_69 Additivi per calcestruzzi e malte Concrete and mortars additives SIRIO SC SIRIO C SIRIO C SIRIO A SIRIOMEL 57 SIRIOMIX SIRIO A SIRIOGEL 50P L AERSIRIO Disarmanti Release agents ALCHIOIL ALCHIOIL ALCHIOIL 200 SR ALCHIOIL NUOVO DISARMOIL EMULSFORM ECOFINISH ECOFINISH MCI PRONTOSFORM PRONTOSFORM MCI RAPIDSFORM RAPIDSFORM FL VIBROSFORM SF 69 SILVERSFORM MCI 69 ORIONE pag. 70_76 Attrezzature Varie Various fittings SCROSTATORE DB 34 - DB SCROSTATORE EB INIETTORI MABI POMPA CHAPIN 73 POMPA MESTO 73 POMPA STAR POMPA STAR P P 7000 AIRLESS 74 P 7000 / S AIRLESS POMPA P / 4200 AIRLESS POMPA W

8 INDICE ALFABETICO ALPHABETICAL INDEX 9 A B C AERSIRIO ALCHIOIL ALCHIOIL ALCHIOIL 200 SR ALCHIOIL BENTOGEO BENTOGEO P BENTOPAN BENTOPOL/PF 39 BENTOTITE BIG BENTOTITE PASTE HR BENTOTITE WATER BAR CHIODI DI FISSAGGIO 40 e 42 (BENTOPAN - BENTOGEO-P - RETE PER KUNISEAL) D E G H I K L DUROKAL ECOFINISH ECOFINISH MCI EMULSFORM M GIUNTOFLEX GIUNTOROLL 46 HYDROMAS HYDROSTOP INIETTORI MABI INTOCAL INTOCAL RINZAFFO 27 INTONACHINO ANTICO KALINZ KUNISEAL LEAKMASTER pag. pag. pag. N P R MARTELLI SCROSTATORI MCI MCI MCI 2020 VO 12 MCI MCI MICROPOZ NUOVO DISARMOIL PASTA DORIT 35 PISTOLA PER GIUNTOFLEX 46 POLYPRIMER PER GIUNTOFLEX 45 POMPA CHAPIN 73 POMPA MESTO 73 POMPA P 4200 AIRLESS P 7000 AIRLESS 74 P 7000 S AIRLESS POMPA STAR P POMPA STAR POMPA W PRONTOSFORM PRONTOSFORM MCI RAPIDSFORM RAPIDSFORM FL RASOCAL (SIRIORETE) RESIVIL RETE PER KUNISEAL 42 RONDELLE 40 (PER FISSAGGIO BENTOPAN - BENTOGEO-P) S SCROSTATORE DB 34 DB SCROSTATORE EB SFERUG SILVERSFORM MCI 69 SIRIO A SIRIO A SIRIO BARRIERA SIRIO BARRIERA W SIRIO BARRIERA WR SIRIOBETON AC SIRIOBETON ADD SIRIOBETON ADD SIRIOBETON ADD SIRIOBETON BME - BME 17 SIRIOBETON BME - BME SIRIOBETON BME - BME SIRIOBETON FA SIRIOBETON FIX R SIRIOBETON FLEX M (SIRIORETE) SIRIOBETON HCR SIRIOBETON HCR SIRIOBETON IDR SIRIOBETON IDR RINZAFFO 28 SIRIOBETON INZ SIRIOBETON PR SIRIOBETON PR MONO SIRIOBETON RA SIRIOBETON RAPID SIRIOBETON RV - RV FINE SIRIOBETON STOP SIRIOBETON STOP SIRIOBIT 53 SIRIO C SIRIO C SIRIO SC SIRIOCRYL - E SIRIOCEM PF SIRIOEPOS SIRIOEPOS SIRIOFIBRE /G 37 (fibre in polipropilene) SIRIOFIBRE MICRO 37 (fibre in poliacrilonitrile) 10/A 20/A V SIRIOGEL 50P L SIRIOMEL 57 SIRIOMIX SIRIONET 35 SIRIOPEL 36 SIRIOSAN SIRIOSEAL SOLVOIL 36 SOLVOIL 53 VIBROSFORM SF 69 TM VCI

9 linea ANDROMEDA Prodotti ad alta resistenza chimica HCR - High chemical resistance products

10 ANDROMEDA Prodotti ad alta resistenza chimica MCI 2000 Additivo inibitore di corrosione migratorio, per calcestruzzi e malte. MCI 2000 è un additivo liquido da aggiungere alle miscele cementizie; MCI 2000 protegge i ferri d armatura con una funzione anticorrosione di molecole che migrano all interno del calcestruzzo e si fissano sulle armature metalliche. MCI 2000 è indicato per tutte le strutture in calcestruzzo armato, prefabbricato, precompresso, post teso, soprattutto se realizzate in ambienti marini o particolarmente aggressivi e soggetti all innesco della corrosione delle armature. MCI 2000.costituisce una soluzione tecnico-economica valida per estendere la durabilità di strutture a piogge acide o soggette alle aggressioni da cloruri per esposizioni marine o per sali decongelanti. Dosaggio 0,75 1,5 Lt. ogni m 3 di calcestruzzo o malta. Fusto da kg 200 Tanica da kg 20. La Proind è distributrice esclusiva per l Italia dei prodotti Cortec dedicati al settore edile. ANDROMEDA Prodotti ad alta resistenza chimica MCI 2020 Inibitore di corrosione migratorio per impregnazione e penetrazione su strutture in cemento armato. MCI 2020 è un inibitore di corrosione, non tossico per l utilizzatore, da applicare su superfici in calcestruzzo per inibire la corrosione delle armature non affioranti. MCI 2020 migra attraverso le porosità del conglomerato fino a raggiungere le armature sulle quali si fissa per proteggerle dalla corrosione causata da Il concetto MCI carbonatazione, azione dei cloruri o da correnti vaganti. Trattamento protettivo ed inibitore di corrosione di strutture in cemento armato aggredite da cloruri, carbonatazione o correnti vaganti. Penetrando profondamente nel calcestruzzo ed autorigenerandosi, permette di realizzare un trattamento d inibizione della corrosione autocondensandosi sul metallo, con elevata durabilità cc per m 2. Taniche da kg 25 e 5. Applicazione A spruzzo, rullo, pennello. Rimuovere il CLS in fase di distacco Il primo passo per inibire la corrosione delle armature non affioranti è quello di rimuovere la parte di CLS degradato e non più monilitica. 11 MCI 2020 migra attraverso il CLS per proteggere i ferri di armatura L inibitore migra ad una profondità considerevole attraverso il CLS sino a depositarsi sopra i ferri di armatura MCI 2020 protegge i ferri di armatura prevenendo future corrosioni L inibitore si fissa ai ferri di armatura costituendo un sottile strato protettivo di molecole MCI. Questo previene la reazione chimica tra l acciaio, l ossigeno e altri composti chimici che si formano normalmente nel CLS degradato se questo non è stato protetto con MCI 2020.

11 ANDROMEDA Prodotti ad alta resistenza chimica TM VCI 325 Inibitore di corrosione migratorio, per superfici metalliche. VCI 325 è un composto pronto all uso a base di speciali oli sintetici protettivi, contenenti specifici additivi migratori inibitori della corrosione, particolarmente adatto al trattamento anticorrosivo dei metalli. TM VCI 325 agisce lasciando fisicamente un velo, con proprietà idrofobiche, sul metallo trattato e migra all interno della porosità del metallo, cosa che lo differenzia da tutti gli altri prodotti. VCI 325 forma un sottile strato protettivo monomolecolare che si auto rigenera grazie alla continua emissione di vapori creatisi in conseguenza dell azione espletata TM dagli ioni VCI garantendo così la massima protezione dalla corrosione. TM VCI 325 è raccomandato per: Acciaio al Carbonio, Acciaio Inossidabile, Ghisa, Leghe di alluminio, Acciaio Zincato, Ottone (< 30%Zn), Rame. VCI 325 è adatto in generale alla protezione di metalli finemente lavorati e trova un impiego particolare nel settore della prefabbricazione per il trattamento anticorrosivo delle superfici metalliche dei casseri e delle attrezzature metalliche. Dette superfici, oltre alla normale usura di utilizzo data dalle continue abrasioni (evidente in particolar modo in determinati punti dei casseri ) sono anche spesso esposte a sbalzi di temperatura ( vapore per la maturazione forzata ) ed agli agenti atmosferici ( piste scoperte e posizionate in aree esterne ), fatti questi che accelerano i processi di ossidazione e corrosione dei metalli che li compongono. Inoltre frequentemente detti casseri vengono fatti oggetto di ripetute saldature e molature, anche in quelle zone più che in altre l ossidazione che si presenta è spesso persistente in relazione alla grossolana finitura che il metallo assume dopo tali operazioni. TM TM TM VCI 325 è un prodotto specificamente formulato che, applicato su superfici metalliche, svolge una profonda e duratura azione protettiva contro la corrosione; è semplice da impiegarsi e l invisibile strato protettivo di ioni VCI non alte- TM ra le proprietà dei metalli trattati allungando la loro vita utile. La sua azione binaria (azione fisica = TM velo protettivo + azione degli ioni VCI = strato monomolecolare inibitore) è quanto di più efficace esista per proteggere i metalli. Dosaggio Da 0,75 a 1 lt. per 40 mq. a seconda del tipo di finitura della superficie del metallo da trattare. Taniche da lt Lastra di metallo trattata con protettivo VCI TM325 Lastra di metallo non trattata Tempo di esposizione agli agenti atmosferici: 30gg. Data inizio: 10/11/03 Data rilevazione: 10/12/03 MCI 2020 VO Versione in polvere MCI 2020 per applicazioni su supefici verticali. Comforme alle specifiche ASTM-G109. MCI 2005 MCI 2006 Additivo di inibitori Migratori di Corrosione per Calcestruzzo, Brevettato. Additivo a base acquosa per prevenire la corrosione dei ferri di armatura ed altri acciai nel calcestruzzo. Disponibile anche in versione NS (normal set/tempo di presa). Conforme al ASTM G-109. Polvere Additivo di Inibitori Migratori di Corrosione Migranti per Calcestruzzo. Additivo in polvere per prevenire la corrosione dei ferri di armatura ed altri acciai nel calcestruzzo. Basata sulla tecnologia MCI Disponibile anche in versione NS (normal set/tempo di presa) 12

12 ANDROMEDA Prodotti ad alta resistenza chimica SIRIOCEM PF Miscela cementizia bicomponente per la protezione dei ferri d armatura dalla corrosione. SIRIOCEM P.F. è una boiacca pennellabile da applicare sui ferri d armatura per inibire o prevenire la formazione di ruggine. SIRIOCEM P.F. consente di realizzare un rivestimento con spessore 2 mm ad elevatissima adesione al ferro ed al calcestruzzo, buone resistenze meccaniche e basso modulo elastico, elevata durabilità alla penetrazione dell acqua o soluzioni saline. SIRIOCEM P.F. è additivato con speciali inibitori di corrosione. Protezione anticorrosiva dei ferri d armatura durante il ciclo di riparazione corticale dei cementi armati, rivestimento protettivo di armature affioranti, protezione dei ferri d armatura a contatto con acqua di mare, barriera anticarbonatazione, boiacca d aderenza tra supporto e nostre malte Siriobeton. Assoluta inibizione e protezione delle armature dalla formazione di ruggine trattate e non ma adiacenti a quelle trattate. ANDROMEDA Prodotti ad alta resistenza chimica SIRIOEPOS 131 Adesivo epossidico per beton plaqué, ripristini del copriferro ed incollaggi strutturali. SIRIOEPOS 131 è un adesivo epossidico bicomponente, senza solventi a consistenza tixotropica, per il consolidamento strutturale di materiali da costruzione (calcestruzzo, mattoni, pietre naturali,). SIRIOEPOS 131 è indicato per consolidamenti strutturali mediante beton plaqué, unione di conci prefabbricati, protezione di armature affioranti, sigillatura e riparazione di lesioni strutturali. Facilità e sicurezza d impiego, perfetta tixotropia ed ottimo potere riempitivo anche in spessore, assenza di ritiro, adesione monolitica anche su superfici umide, elevate e rapide resistenze meccaniche anche alle basse temperature, assoluta impermeabilità all acqua, resistente agli agenti chimici e all invecchiamento atmosferico, notevoli qualità dielettriche, totali proprietà anticorrosione. ANDROMEDA Prodotti ad alta resistenza chimica SIRIOEPOS 552 Resina epossidica bicomponente per iniezioni di consolidamento. SIRIOEPOS 552 è un adesivo epossidico bicomponente, senza solventi, a bassissima viscosità, per il consolidamento di strutture mediante iniezione a bassa pressione. Iniezione in fessure anche capillari e diffuse, sigillature e colature di incorporazione, incollaggi strutturali e beton plaqué.. Notevole effetto impregnante e di consolidamento in profondità, ottimo potere di migrazione anche in fessure sottili (0,3 mm), adesione monolitica anche su superfici umide, elevate e rapide resistenze meccaniche anche alle basse temperature, stabilità volumetrica, assoluta impermeabilità all acqua, elevata resistenza agli aggressivi chimici ed all invecchiamento. 13

13 ANDROMEDA HCR - High chemical resistance products Two components special powder formulation providing high grade of passivation 60 gr/ml/tondo Ø 10 mm per singola applicazione. Secchiello per complessivi kg 4 (A 3kg + B 1kg). Applicazione a pennello. SIRIOCEM PF Special powder formulation based on hydraulic binders complexing and osmotic agents and components providing high grade of passivation. The mix contains corrosion inhibitors. SIRIOCEM P.F. provides valid protection of the iron against oxidizing agents, where it has been applied its molecules migrate toward the concrete so ionizing also adjacent steel surfaces that are not directly treated. Technical data Colour: grey. Coverage: 60 gr linear meter for a 10 mm diam round bar for each single application Application Brush Part A 3 kg + part B 1 kg = 4 kg drums ANDROMEDA HCR - High chemical resistance products Epoxy adhesive resin 1,6 kg/m 2 /mm. Applicazione a spatola o pennello. Pot life 1Kg di resina: 30 min. a 20 SIRIOEPOS 131 Two components, solvent free for the repairs of different building materials like concrete, brick, stone. It s very easy to use and assure a perfect adhesion of different age concretes. Technical data Paste version. Coverage: 1,6 kg/m 2 /mm Pot life 1 kg: 30 minutes at 20 c 3 kg (A + B) units Barattoli per complessivi 3 kg (A+B). ANDROMEDA HCR - High chemical resistance products Two component epoxy resin for injections for monolithic repairs of cracked structures. Pot life 0,5 kg 20 min. a 20 Peso specifico 1,1 Kg/l a 20 Barattoli per complessivi 2 kg (A+B). SIRIOEPOS 552 SIRIOEPOS 552 is a two-part superfluid epoxy adhesive, solvent-free, for bonding and structural reinforcement by low pressure injection. Applications Injections for sealing cracks in cement screeds, also capillar and diffused ones, bonding and pouring incorporations, beton plaquè (bonding steel plates to concrete). High penetration with a deep consolidating action, sealing of thin cracks ( 0,3mm.), monolithic adhesion also in moist structures. High and rapid response with mechanical resistance at low temperatures, volumetric stability, absolute watertight after hardening, high resistance to chemicals agents, long lasting durability. Pot life 0,5 kg 20 min. at 20 S.g. 1,1 kg/l at 20 2 kg. (A+B) units 14

14 ANDROMEDA Prodotti ad alta resistenza chimica SIRIOBETON HCR 10 Malta reoplastica antiritiro ad alta resistenza chimica. SIRIOBETON HCR 10 è una miscela cementizia perfettamente colabile ed antiritiro. Riempimenti e consolidamenti eseguiti con SIRIOBETON HCR 10 sono caratterizzati da altissima adesione, durabilità, impermeabilità, eccezionali resistenze meccaniche ed all abrasione, elevata resistenza alle aggressioni chimiche, elevata resistenza ai cicli gelo disgelo, ed alle correnti vaganti. Operazioni di getto in cassero ove sussistano aggressioni chimiche ed in particolare cloruri solfati e nitrati, o dove siano richieste elevate resistenze alla compressione e sfilamento. Realizzazione e riparazione di pavimenti antiabrasione nelle industrie chimiche e lattiero casearie. Elevata lavorabilità e fluidità, assenza di bleeding e stabilità volumetrica, fortissima adesione al substrato ed elevate resistenze chimico meccaniche, elevata durabilità alle aggressioni chimiche ed all acqua anche in pressione. ANDROMEDA Prodotti ad alta resistenza chimica SIRIOBETON HCR 20 Malta antiritiro fibrorinforzata per ripristini verticali strutturali ad alta resistenza chimica. SIRIOBETON HCR 20 è una miscela cementizia tixotropica fibrorinforzata ed antiritiro, perfettamente lavorabile a cazzuola o intonacatrice: I ripristini eseguiti con SIRIOBETON HCR 20 sono caratterizzati da altissima adesione, durabilità, impermeabilità, eccezionali resistenze meccaniche ed all abrasione, elevata resistenza alle aggressioni chimiche, elevata resistenza ai cicli gelo disgelo, elevata resistività alle correnti vaganti. Ripristini e bonifiche del copriferro in ambienti aggressivi o sottoposti a frequenti cicli gelo disgelo, intonaci e consolidamenti strutturali di dighe o sponde di canali, viadotti o ponti autostradali e ferroviari. Rapidità e facilità applicativa in verticale o soffittature, elevate resistenze meccaniche, forte ed immediata adesione al supporto, elevati spessori applicabili (4 6 cm) caratterizzati da stabilità volumetrica, elevata durabilità alle aggressioni chimiche ed all acqua anche in pressione. ANDROMEDA Prodotti ad alta resistenza chimica MICROPOZ Microsilicati densificati. MICROPOZ, comunemente chiamata silica fume o microsilicati, è un prodotto derivato dal processo di riduzione della quarzite durante la produzione di leghe ferro silicio. Attraverso la fase di captazione del biossido di silicio attraverso appositi filtri si ottiene una polvere con caratteristiche quali l'elevata finezza, una forma sferica, una struttura amorfa con dimensioni di 0,1 micron. Ovunque sia richiesto un calcestruzzo a prestazione con caratteristiche di elevata resistenza impermeabilità e durabilità. Ideale anche per realizzare getti subacquei in presenza di acqua di falda. Consistente incremento delle resistenze meccaniche,notevole riduzione della penetrazione dei cloruri e della carbonatazione, cospicuo incremento della resistività elettrica con conseguente elevato potere anticorrosione. 15

15 ANDROMEDA HCR - High chemical resistance products Rheoplastic mortar, anti-shrink with high resistance against chemical agents. 19 kg/m 2 /cm Ø max inerte. 1,5 mm Sacchi da kg 25 Acqua d impasto 13% SIRIOBETON HCR 10 SIRIOBETON HCR 10 is a cement mix perfectly pourable anti-shrink. The structural repairing and reinforcing made with SIRIOBETON HCR 10 are characterized from an exeptional mechanical strenght, high resistance against corrosion, salts, freeze-thaw cycles, abrasion, waterproof and excellent adhesion. Application Concrete pourings in forms where subsist attacks from chemical agents (sulphates, nitrates, chlorides) and there are requested high resistance to compression and a very good grip action against the unthreading. For new floors and to repair old floor where is requested high resistance to chemicals (chemical firms, central dairys) Very fluid, easy to work, bleeding free, very high adhesion to the substratum and exeptional chemical and mechanical strengths, high resistance to chemical agents and water pressure. Consumption 19 Kg. of SIRIOBETON HCR 10 each square meter per 1 cm. of thickness, diam. max. of the aggregates that is possible to add: 1,5 mm. Sacks 25 Kg. Water mix: 13%. ANDROMEDA HCR - High chemical resistance products Fiber reinforced rheoplastic mortar, shrink-proof with high resistance against chemical agents. 19 kg/m 2 /cm Ø max inerte. 1,5 mm Sacchi da kg 25 Acqua d impasto 10% SIRIOBETON HCR 20 SIRIOBETON HCR 20 is a thixotropic cement mix anti-shrink with fibers added to improve its force against little cracks. The structural repairing and reinforcing made with SIRIOBETON HCR 20 are characterized from an exceptional mechanical strenght, high resistance against corrosion, salts, freeze-thaw cycles, abrasion, waterproof and excellent adhesion. Applications To restore concretes, expecially the surface of the concretes (2-4 cm. over the reinforcing rods) that need to be to repaired or reinforced. SIRIOBETON HCR 20 found a proper application in restoring works of dikes, canalizations, pipes, bridges, viaducts of railroads or motorways. Easy to work, bleeding free, very rapid application and high adhesion to the substratum, exeptional chemical and mechanical strengths, high resistance to chemical agents and water pressure, high thickness for a single application ( 4-6 cm.). Consumption 19 Kg. of SIRIOBETON HCR 20 each square meter per 1 cm. of thickness, diam. max. of the aggregates that is possible to add: 1,5 mm. Sacks 25 Kg. Water mix: 10% ANDROMEDA HCR - High chemical resistance products High density microsilicates. Dosaggio 8 15% sul peso del cemento. Big Bag da 1200 kg oppure sacco da 20 e 25 kg MICROPOZ MICROPOZ, usually known as silica fume or simply as microsilicate, is a by-product from reduction process of qartzite during the production of metal silicon. During the getting of silicon dioxid with proper special filters it is separated a powder with particular characteristics: sferic shape, amorfous structure with only 0,1 micron diameter. High increasing of the mechanical strength, consistant reduction of the permeability to chlorides and the effects of carbonation, very good anticorrosion effects. Applications For the production of every concrete where is requested a very high resistance in waterproofing and in durability. It is reccomended when you have to pour concrete in sites with water-bearing stratum and in under water works. Dosage 8 15 % of cement weight. Big bags of Kg, sacks Kg. 16

16 ANDROMEDA Prodotti ad alta resistenza chimica SIRIOBETON BME Malta bicomponente antiritiro fibrorinforzata a basso modulo elastico. SIRIOBETON BME è una miscela cementizia bicomponente tixotropica fibrorinforzata ed antiritiro, perfettamente lavorabile a cazzuola o intonacatrice: Gli strati eseguiti con SIRIOBETON BME sono caratterizzati da altissima adesione, durabilità, impermeabilità, elevate resistenze meccaniche ed all abrasione, elevata resistenza alle aggressioni chimiche, elevata resistenza ai cicli gelo disgelo, basso modulo elastico, buona permeabilità al vapore acqueo. Ripristini e bonifiche del copriferro in ambienti aggressivi o sottoposti a frequenti cicli gelo disgelo o sollecitazioni da traffico, intonaci e consolidamenti strutturali di dighe o sponde di canali, viadotti o ponti autostradali e ferroviari, ripristino di pavimenti in calcestruzzo, rasature anticarbonatazione ed impermeabilizzanti di strutture in cemento armato. ANDROMEDA HCR - High chemical resistance products Rapidità e facilità applicativa in verticale, su soffittature o pavimentazioni, elevate resistenze meccaniche, forte ed immediata adesione al supporto, possibilità di realizzare spessori variabili da 1 a 30 mm, per singola applicazione, caratterizzati da stabilità volumetrica, elevata durabilità alle aggressioni chimiche e meccaniche, elevata impermeabilità all acqua anche in pressione. 20 kg/m 2 /cm Ø max inerte 1,2 mm. Da kg 30,25 (A 25 kg + B 5,25 kg) Super adhesive thixotropic shrink-proof rheoplastic mortar fiber reinforced, low elasticity modulus. SIRIOBETON BME Super adhesive thixotropic shrink-proof rheoplastic mortar fiber reinforced with hight protection and durability very low elasticity modulus, for repair and finishing of spalled concretes and masonries. It contains corrosion inhibitors.siriobeton BME Is a cement formulation consisting of ready-mixed powder and special liquid resin no-toxic recommended for all types of repair or restoration of damaged concretes. Technical data Initial setting times: about 30 minutes at 25 c. Colour: grey. Application thickness: from 1 to 30 mm. Working time per mix: 15 minutes. Coverage: 2 kg/m 2 per mm of thickness. Mix ratio (two components): Part. A kg 25 + part. B kg 5,25. Application trowel or pump. Part. A kg 25 sacks + part. B kg 5,25 drum. 17

17 linea SIRIO Malte cementizie antiritiro e a base calce - Formulati speciali - Fibre Controlled shrinkage, cement and lime based, mortars - Special compounds - Fibers

18 SIRIO Malte cementizie antiritiro e a base calce SIRIOBETON RV - RV FINE Malte antiritiro fibrorinforzate per ripristini verticali strutturali. SIRIOBETON RV e RV FINE sono miscele cementizie tixotropiche fibrorinforzate ed antiritiro, perfettamente lavorabili a cazzuola o intonacatrice. I ripristini eseguiti con SIRIOBETON RV e RV FINE sono caratterizzati da altissima adesione, durabilità, impermeabilità, eccezionali resistenze meccaniche. Ripristini e bonifiche del copriferro, intonaci e consolidamenti strutturali. Rapidità e facilità applicativa in verticale o soffittature, elevate resistenze meccaniche, forte ed immediata adesione al supporto, elevati spessori applicabili R.V. (1 5 cm), R.V./FINE (2 mm 1 cm) caratterizzati da stabilità volumetrica. SIRIO Malte cementizie antiritiro e a base calce SIRIOBETON FA Malta antiritiro fibrorinforzata per ripristini verticali strutturali a base di microsilicati. SIRIOBETON FA è una miscela cementizia tixotropica fibrorinforzata ed antiritiro, additivata con microsilicati, perfettamente lavorabile a cazzuola o intonacatrice: I ripristini eseguiti con SIRIOBETON FA sono caratterizzati da altissima adesione, durabilità, impermeabilità, eccezionali resistenze meccaniche ed all abrasione, resistenza a soluzioni contenenti cloruri, nitrati o solfati, elevata resistenza ai cicli gelo disgelo, elevata resistività alle correnti vaganti. Ripristini e bonifiche del copriferro in ambienti aggressivi o sottoposti a frequenti cicli gelo disgelo, intonaci e consolidamenti strutturali di dighe o sponde di canali, viadotti o ponti autostradali e ferroviari. Rapidità e facilità applicativa in verticale o soffittature, elevate resistenze meccaniche, forte ed immediata adesione al supporto, elevati spessori applicabili (1 8 cm) caratterizzati da stabilità volumetrica, elevata durabilità alle aggressioni chimiche SIRIO Malte cementizie antiritiro e a base calce SIRIOBETON RA MONO Malta antiritiro bicomponente per rasature. SIRIOBETON RA MONO è una miscela cementizia bicomponente antiritiro, perfettamente lavorabile a cazzuola o spatola metallica: Gli strati eseguiti con SIRIOBETON RA MONO sono caratterizzati da altissima adesione, durabilità, impermeabilità, elevate resistenze meccaniche ed all abrasione, elevata resistenza alle aggressioni chimiche, elevata resistenza ai cicli gelo disgelo, buona permeabilità al vapore acqueo, elevato grado di finitura. Sigillatura rigida di crepe, protezione del copriferro in ambienti aggressivi o sottoposti a frequenti cicli gelo disgelo o sollecitazioni da traffico, rivestimenti di dighe o sponde di canali, viadotti o ponti autostradali e ferroviari, rasature anticarbonatazione ed impermeabilizzanti di strutture in cemento armato. Rapidità e facilità applicativa, elevate resistenze meccaniche, forte ed immediata adesione al supporto, possibilità di realizzare spessori variabili da 0,3 a 5 mm caratterizzati da stabilità volumetrica, elevata durabilità 19

19 SIRIO Controlled-shrinkage, cement and lime based, mortars Rheoplastic mortar, compensated shrinkage, fiber reinforced kg/m 2 /cm Ø max inerte. R.V. 1,5 mm R.V. FINE 0,3 mm. Sacchi da kg 25 Acqua d impasto R.V Lt. per 100 kg. R.V. FINE Lt. per 100 kg. SIRIOBETON RV - RV FINE Rheoplastic mortar, fiber reinforced ready to use for structural repairs with compensated shrinkage and normal setting time. This product doesn t contain metallic elements. Excellent adhesion, making it easy to spread on vertical surfaces resistant to chemical attack and excellent impermeability to water penetration. Technical data Initial setting times: about 1 hour at 25 c Colour: grey. Application thickness: from 10 to 30 mm. Working time per mix: 30 minutes. Coverage 1,8 1,9 kg/m 2 per mm of thickness. Mix ratio:16 18 lt water per 100 kg of dry mix R.V. FINE. R.V lt. Application Trowel or pump. 25 kg sacks. SIRIO Controlled-shrinkage, cement and lime based, mortars Microsilica rheoplastic mortar fiber reinforced. ed all acqua anche in pressione kg/m 2 /cm Ø max inerte. 1,5 mm Sacchi da kg 25 Acqua d impasto 14 18%. SIRIOBETON FA Excellent adhesion, making it easy. Suitable for waterproofing restorations, recostructions. Silica fume greatly improves resistance to corrosion, salt, freeze-thaw cycling, abrasion and reduces permeability. Technical data Initial setting times: about 1 hour at 25 c Colour: grey. Application thickness: from 10 to 60 mm. Working time per mix: 20 minutes. Coverage 1,6 1,8 kg/m 2 per mm of thickness. Mix ratio: lt water per 100 kg of dry mix. Application Trowel or pump. 25 kg sacks. SIRIO Controlled-shrinkage, cement and lime based, mortars Two component antishrink smoothing mortar. alle aggressioni chimiche e meccaniche, elevata impermeabilità all acqua anche in pressione, elevato grado di finitura. 2,1 kg/m 2 /mm Ø max inerte. 0,3 mm Sacchi da kg 25 SIRIOBETON RA MONO SIRIOBETON RA MONO is a two component cement mix shrink-free smoothing mortar. SIRIOBETON RA MONO has a great resistance to corrosion, salts, freeze-thaw cycles, abrasion and at the same time guarantee a good level of transpiring to the structure finished with this particular smoothing mortar. Its shrinkage-free consent to obtain a volumetric stability, the high level of smooth finishing it s combined to an excellent adhesion. Applications Finishing smooth coats in general applications on concrete walls and in restoration of dikes, canalizations, bridges, rail-roads and motorway viaducts. Easy and fast to be applied, high adhesion for a single application from 0,3 to 5 millimeters. Consumption 2,1 Kg./ m 2 per mm. of thickness. 25 kg sacks. 20

20 SIRIO Malte cementizie antiritiro e a base calce SIRIOBETON FIX - R Malta reoplastica antiritiro per riparazioni e fissaggi a rapidissimo indurimento. SIRIOBETON FIX - R è una malta reoplastica monocomponente con sufficiente tempo di lavorabilità e posa in opera, ma a rapidissimo indurimento e con elevate resistenze meccaniche già dopo 1 ora dall applicazione. Rapidi ripristini e bonifiche del copriferro, sigillatura di buchi e lesioni, bloccaggio e fissaggio di tiranti, cardini, pozzetti e chiusini. Rapidità e facilità applicativa, rapidissimi tempi d indurimento con ottenimento di elevate resistenze meccaniche alle brevi stagionatue, assenza di ritiro e buona adesione al supporto. 19 kg/m 2 /cm Ø max inerte. 1,2 mm Sacchi da kg 25 e 5 Acqua d impasto 14 18%. SIRIO Malte cementizie antiritiro e a base calce SIRIOBETON AC Malta reoplastica antiritiro a colare. SIRIOBETON AC è una miscela cementizia a stabilità volumetrica perfettamente colabile in cassero. SIRIOBETON AC consente di ottenere conglomerati ad altissima adesione, durabilità, impermeabilità, con elevate resistenze meccaniche. SIRIOBETON AC è indicato per inghisaggi di basamenti di macchinari, ancoraggi di colonne in calcestruzzo o acciaio, ripristini e risanamenti di pavimentazioni, consolidamenti strutturali di sottomurazioni o pilastri. Elevata lavorabilità e fluidità, assenza di bleeding e stabilità volumetrica, fortissima adesione al substrato ed elevate resistenze chimico meccaniche. SIRIO Malte cementizie antiritiro e a base calce SIRIOBETON INZ Prodotto in polvere per iniezioni di boiacche antiritiro. SIRIOBETON INZ è una miscela cementizia opportunamente additivata per ottenere boiacche ad altissima fluidità, durabilità, impermeabilità, elevate resistenze meccaniche, elevata resistenza ai cicli gelo disgelo, buona permeabilità al vapore acqueo. Permeazione e consolidamento di conglomerati porosi ed incoerenti; sigillatura di conglomerati ghiaiosi o cementizi, riempimento di guaine di cavi sottoposti a post tensione, di cavità per tiranti d ancoraggio, guaine. Consolidamento mediante iniezione in murature e sottomurazioni. Assenza di ritiro e bleeding, elevate resistenze meccaniche, elevata fluidità e penetrazione a pressione in crepe e fessure molto sottili, perfetta adesione alle armature ed al supporto, lunghi tempi d iniettabilità. 21

21 SIRIO Controlled-shrinkage, cement and lime based, mortars Rheoplastic mortar for repair super quick setting. SIRIOBETON FIX - R For horizontal or vertical surfaces used for quikly restorations and applications. It is specifically formulated to repair pre-cast concrete and masonry when rapid setting is necessary. Technical data Initial setting times: about 10 minutes at 20 c Colour: grey. Application thickness: from 10 to 30 mm. Working time per mix: 5 minutes. Coverage: 1,9 kg/m 2 per mm of thickness. Mix ratio: lt water per 100 kg of dry mix. Application Metal trowel. 5 e 25 kg sacks. SIRIO Controlled-shrinkage, cement and lime based, mortars Rheoplastic anti-shrink self-levelling compound kg/m 2 /cm Ø max inerte. 2,5 mm. Sacchi da kg 25 Acqua d impasto 11 13%. SIRIOBETON AC SIRIOBETON AC is a cement mix ready to use. After mixing with water, it is perfectly pourable and gives mixes of the highest adherence. Durability with exceptional mechanical strength and pratically no shrinkage. Free of metallic components. Technical data Initial setting times: about 1 hour at 25 c Colour: grey. Working time per mix: 30 minutes. Coverage: 1,6 1,8 kg/m 2 /mm Mix ratio: lt water per 100 kg of dry mix. Application Trowel or pump. 25 kg sacks. SIRIO Controlled-shrinkage, cement and lime based, mortars Cement based powder for injecting as rheoplastic shrink free grout. 1,9 kg/dm 3. Sacco da kg 20. Acqua d impasto 30%. SIRIOBETON INZ SIRIOBETON INZ produces a very high mechanical strength grout, that does not shrink or "bleed". Very fluid easy to inject into holes, crevices craks and porous conglomerates. Prevents "stress corrosion" in steel wires under tension. Technical data Working time per mix: pumpable from 1 to 2 hours. Mix ratio: 30 lt water for 100 kg of dry mix. Consumption 1,9 kg/dm kg sacks. Free of metals expanders 22

22 SIRIO Malte cementizie antiritiro e a base calce SIRIOBETON BME Malta bicomponente antitiriro fibrorinforzata a basso modulo elastico. SIRIOBETON BME è una miscela cementizia bicomponente tixotropica fibrorinforzata ed antiritiro, perfettamente lavorabile a cazzuola o intonacatrice: Gli strati eseguiti con SIRIOBETON BME sono caratterizzati da altissima adesione, durabilità, impermeabilità, elevate resistenze meccaniche ed all abrasione, elevata resistenza alle aggressioni chimiche, elevata resistenza ai cicli gelo disgelo, basso modulo elastico, buona permeabilità al vapore acqueo. Ripristini e bonifiche del copriferro in ambienti aggressivi e sottoposti a frequenti cicli gelo disgelo o sollecitazioni da traffico, intonaci e consolidamenti strutturali di dighe o sponde di canali, viadotti o ponti autostradali e ferroviari. Ripristino di pavimenti in calcestruzzo, rasature anticarbonatazione ed impermeabilizzanti di strutture in cemento armato. Rapidità e facilità applicativa in verticale, su soffittature o pavimentazioni, elevate resistenze meccaniche, forte ed immediata adesione al supporto, possibilità di realizzare SIRIO Malte cementizie antiritiro e a base calce SIRIOBETON PR Malta antiritiro a presa rapida per ripristini, fissaggi e sigillature. SIRIOBETON PR è una miscela cementizia a stabilità volumetrica perfettamente lavorabile a cazzuola. La presa rapida della malta consente la finitura entro 5 10 minuti; gli strati induriti risulteranno ad altissima adesione, durabilità, impermeabilità, con elevate resistenze meccaniche sia dopo poche ore sia alle lunghe stagionature. Riparazioni localizzate di strutture in cemento armato carbonatato o danneggiato in fase di movimentazione nel cantiere di prefabbricazione. Rapidità e facilità d impiego, rapidissimi tempi d indurimento con ottenimento di elevate resistenze meccaniche alle brevi stagionature, assenza di ritiro e buona adesione al supporto SIRIO Malte cementizie antiritiro e a base calce SIRIOBETON PR MONO Malta antiritiro monocomponente a presa rapida per piccole rasature. SIRIOBETON PR MONO è una miscela cementizia monocomponente antiritiro a presa rapida, perfettamente lavorabile a cazzuola o spatola metallica: Gli strati eseguiti con SIRIOBETON PR MONO sono caratterizzati da presa rapida, altissima adesione, durabilità, impermeabilità, elevate resistenze meccaniche ed all abrasione, elevata resistenza alle aggressioni chimiche, elevata resistenza ai cicli gelo disgelo, buona permeabilità al vapore acqueo, elevato grado di finitura. Sigillatura rigida di crepe, omogeneizzazione superfici ripristinate in spessore con SIRIOBETON PR, rasature e stuccature protettive con limitate dimensioni. Rapidità e facilità applicativa, elevate resistenze meccaniche, forte ed immediata adesione al supporto, possibilità di realizzare spessori variabili da 0,3 a 5 mm caratterizzati da stabilità volumetrica, elevata durabilità alle aggressioni chimiche e meccaniche, impermeabilità 23

23 spessori variabili da 1 a 30 mm, per singola applicazione, caratterizzati da stabilità volumetrica, elevata durabilità alle aggressioni chimiche e meccaniche, elevata impermeabilità all acqua anche in pressione. 20 kg/m 2 /cm Ø max inerte 1,2 mm. Part. A kg 25 + part. B kg 5,25 SIRIO Controlled-shrinkage, cement and lime based, mortars Super adhesive thixotropic shrink-proof rheoplastic mortar fiber reinforced with low elasticity modulus. SIRIOBETON BME Super adhesive thixotropic shrink-proof rheoplastic mortar fiber reinforced with high protection and durability very low elasticity modulus, for repair and finishing of spalled concretes and masonries. SIRIOBETON B.M.E. Is a cement formulation consisting of ready-mixed powder and special liquid resin no-toxic recommended for all types of repair or restoration of damaged concretes. Technical data Initial setting times: about 30 minutes at 25 c. Colour: grey. Application thickness: from 1 to 30 mm. Working time per mix: 15 minutes. Coverage: 2 kg/m 2 per mm of thickness. Mix ratio (two components): Part. A kg 25 + part. B kg 5,25 Application Trowel or pump. Part. A kg 25 sacks + part. B kg 5,25 drum SIRIO Controlled-shrinkage, cement and lime based, mortars Rapid grip shrink-proof mortar for restoration, filling and sealing. 19 kg/m 2 /cm Ø max inerte 1,5 mm. Sacchi da kg 25. Acqua d impasto 12 14%. SIRIOBETON PR Rapid grip shrink-proof mortar for restoration, filling and sealing ready-touse cement mix which after mixing with water is very easy to apply. Its rapid grip means you can finish the job within 5 to 10 minutes; does not contain metal components. Hardened layers of this product provide high level of adhesion, long life, impermeableness and high resistance whether after only a few hours or when well weathered. Technical data Initial setting times: about 10 minutes at 20 c Colour: grey. Application thickness: from 10 to 30 mm. Working time per mix: 5 10 minutes. Coverage: 1,9 kg/m 2 per mm of thickness. Mix ratio: lt water per 100 kg of dry mix. Application Metal trowel. 25 kg sacks. SIRIO Controlled-shrinkage, cement and lime based, mortars all acqua anche in pressione, elevato grado di finitura. SIRIOBETON PR MONO è realizzato in 3 differenti colorazioni (grigio, grigio chiaro, grigio 1 ) per ottenere finiture con colore identico a quelle del calcestruzzo su cui viene applicato. 1,9 kg/m 2 /mm Ø max inerte 0,3 mm. Sacco da kg 25. Acqua d impasto 14 %. Rapid grip shrink-proof mortar for restoration, work, filling and sealing. SIRIOBETON PR MONO Rapid grip shrink-proof mortar for restoration, filling and sealing ready-to-use cement mix which after mixing with water is very easy to apply. Hardened layers of this product provide high level of adhesion, long life, impermeableness and high resistance wheter after only a few hours or when well weathered. Technical data Initial setting times: about 10 minutes at 20 c Colour: grey, light grey, grey 1. Application thickness: from 0,3 to 5 mm each coat. Working time per mix: 5 10 minutes. Coverage: 1,9 kg/m 2 per mm of thickness. Mix ratio: 14 lt water per 100 kg of dry mix. Application Metal trowel. 25 kg sacks. 24

24 SIRIO Malte cementizie antiritiro e a base calce SIRIOBETON STOP Malta per bloccare istantaneamente le infiltrazioni d acqua SIRIOBETON STOP è una miscela cementizia a rapidissima presa usata per fermare istantaneamente le infiltrazioni d acqua anche in pressione. SIRIOBETON STOP solidificando anche sott acqua si espande e diventa un corpo unico con il calcestruzzo. Sigillature ermetiche ed istantanee di infiltrazioni d acqua in calcestruzzi. Rapidissimo indurimento anche sott acqua, eccezionali resistenze meccaniche e fortissima adesione al supporto, elevatissima impermeabilità all acqua in pressione. 19 kg/m 2 /cm Secchia da kg 5, Acqua d impasto 22%. SIRIO Malte cementizie antiritiro e a base calce SIRIOBETON FLEX M Composto cementizio bicomponente elastoflessibile impermeabile. SIRIOBETON FLEX M è una miscela bicomponente impermeabilizzante ad elevata adesione ai più svariati supporti, elevato grado di deformazione e potere anticorrosivo delle armature. Rasature flessibili su supporti fessurati con lesioni postume di 1 1,5 mm, rivestimento impermeabilizzante anticarbonatazione e protettivo di strutture in calcestruzzo soggette a sollecitazioni da traffico ed aggressione da sali decongelanti. Impermeabilizzazione di balconi o terrazzi mediante incollaggio di nuove piastrelle direttamente su quelle esistenti e degradate, rivestimento impermeabilizzante di vasche o piscine, sigillatura di crepe o cavità. Facile e veloce applicazione, elevata flessibilità e deformabilità, eccezionale adesione ai più svariati materiali da costruzione, ottima durabilità alla carbonatazione ed ai sali decongelanti, impermeabilità elevata ma 25

25 SIRIO Controlled-shrinkage, cement and lime based, mortars A special cement formulation hydraulic waterstop. SIRIOBETON STOP A special cement formulation hydraulic waterstop blocks running water when applied to holes in masonry or concrete structures. This special formulation allows to obtain high strength and rapid setting while repelling water. Resists chemical attack. Demonstrates exceptional resistance to corrosive action of sulfates. Technical data Initial setting times: about 3 5 minutes. Colour: grey. Working time per mix: 2 minutes. 5 kg. pails. SIRIO Controlled-shrinkage, cement and lime based, mortars buona permeabilità al vapore acqueo, elevato potere anticorrosivo delle armature non affioranti. N.B.: Si consiglia l utilizzo di Siriorete per meglio prevenire possibili microlesioni (Particolari dilatazioni termiche, movimenti strutturali). 3 4 kg/m 2 / 2,5 mm. Elastoplastic two component flexible cement waterproof mortar. SIRIOBETON FLEX M Elastoplastic two component flexible cement mortar for waterproofing balconies terraces, bathrooms, old or new. Technical data Initial setting times: about 1 hour at 20 c Working time: 30 minutes at 20 c. Coverage: 3 4 kg/m 2 / 2,5 mm Mix ratio: a+b 2,5 to 1. Application Flat trowel. Part A 25 kg powder sacks part B 6,5 kg drum Parte A sacchi da 25kg, parte B bidone da 6,5 kg. Siriorete: Rotolo 100 ml. h 1000 mm Maglia 0,5x0,4mm 26

26 SIRIO Malte cementizie antiritiro e a base calce INTOCAL Intonaco minerale traspirante per restauro in edifici storici. L intonaco minerale INTOCAL è una formulazione inorganica che si ispira alle migliori tradizioni dell arte edilizia della nostra storia medioevale e rinascimentale unendo ad esse la possibilità di conoscenza materiali, di misura e di controllo e costanza di qualità, rese possibili dalle moderne tecnologie. Il prodotto SIRIO Malte cementizie antiritiro e a base calce Controlled-shrinkage, cement and lime based, mortars INTOCAL RINZAFFO Intonaco minerale a base calce. Mineral plaster lime-based. INTOCAL RINZAFFO si utilizza per operazioni di rinzaffo prima di intervenire con INTO- CAL, che dovrà essere utilizzato dopo almeno 24 ore dalla mano di applicazione di INTOCAL RINZAFFO Sacchi da Kg 25 è altamente traspirante. Particolarmente indicato per applicazioni negli edifici storici e per il restauro in genere, date le sue caratteristiche fisico-meccaniche e di traspirabilità ed al fatto che è possibile realizzare i colori a campione. Intonaci da applicare sia all esterno che all interno, con i metodi tradizionali anche It s a mineral plaster limebased. INTOCAL RINZAFFO it s used for making roughing-in coat before to apply INTOCAL, that will be possible at least 24 hours from the application of INTOCAL RINZAFFO. per spessori unitari notevoli (15 20 mm per strato). La finitura eseguita a frattazzo consentirà una superficie leggermente "scabra" però già esteticamente valida nella tipologia di molti edifici storici o rustici kg/mq/cm Sacchi da kg 25 Sacks 25 Kg. SIRIO Malte cementizie antiritiro e a base calce SIRIOBETON IDR Intonaco deumidificante idrorepellente. Il SIRIOBETON IDR è un intonaco che consente di ottenere un elevatissima proprietà deumidificante e di risanamento della muratura, ed è formulato in modo tale che il rivestimento sia idrorepellente. Dovunque sia necessario applicare un rivestimento con elevato potere deumidificante per risanare le murature danneggiate dall umidità ascendente. Elevato grado di lavorabilità e di finitura, elevata resistenza ai cicli di gelo/disgelo ed ottima durata nel tempo, assenza di sali efflorescenti, compatibilità con rivestimenti o pitturazioni altamente traspiranti. 27